SS 304H is non-magnetic in the toughened condition. However, they can turn out to be somewhat attractive because of their cold working or welding ability. It tends to be effectively welded and handled by standard shop creation rehearses. These have general corrosion resistance, and it opposes air consumption, just as decently oxidizing and lessening conditions. Also, because of its high carbon content, SS 304 Sheets and 304L Coils depend on carbide precipitation in the welds Heat zone of welds.
Our Company offered SS 304 Sheets are the unique specifications and working aspects. The manufacture and production are done by following the latest specifications and methods that help us offer the best qualitative Coils and Sheets. We use the best components and elements that offer great finishes. The variations and forms of these products are available in unique forms and sectors such as dimensions, shapes, latest sizes, and norms.
What type of material is used?
• Stainless steel
Different Properties and Characteristics:
• Mechanical Properties: Ultimate Tensile Strength, Elongation, Reductions, Hardness, and Rockwell
• Physical Properties: Density, Specific Heat, Thermal conductivity, Modulus of Elasticity, Melting range, and Electrical Resistivity.
Industries that use SS 304 Plates, Sheets, and Coils:
• Chemical Industry and Petrochemical processing pressure vessels
• Tanks and Piping systems
• Heat Exchangers
• Flanges and Fittings
• Petroleum Refining
SS 304 Sheets have a higher carbon content while making the steel more appropriate for use in applications where higher temperatures are available. SS 304H Plate is an austenitic chromium-nickel steel amalgam. It has a more prominent carbon content that conveys an expanded yield strength and rigidity. The material used for the 304H Sheet is highly qualitative and suggested for use in a wide range of applications.
Most plates and coils contain the consumption obstruction that will generally be equivalent in most dangerous conditions. Therefore, conditions that are adequately destructive to cause intergranular consumption of welds and heat-affected zones should be utilized in light of its low carbon content.
|Specifications||ASTM A240, ASME SA240|
|Dimensional specification||JIS, AISI, ASTM, GB, DIN, EN, etc|
|Width||1000mm, 1219mm, 1500mm, 1800mm, 2000mm, 2500mm, 3000mm, 3500mm, etc|
|Length||2000mm, 2440mm, 3000mm, 5800mm, 6000mm, etc/td>|
|Thickness||0.3 mm to 120 mm|
|Form||Coils, Foils, Rolls, Plain Sheet, Shim Sheet, Perforated Sheet, Chequered Plate, Strip, Flats, Blank (Circle), Ring (Flange) etc.|
|Surface Finishing||Hot rolled plate (HR), Cold rolled sheet (CR),2B, 2D, BA, NO.1, NO.4, NO.8, 8K, mirror, Chequered, embossed, hair line, sand blast, Brush, etching, SATIN (Met with Plastic Coated) etc.|
|Value Added Services||Cutting, Beveling, Polishing, Threading, Destructive, Non Destructive, Ultrasonic Testing|
|Outside Finish||Finish as per customer Requirements|
|Delivery Condition||Annealed and Pickled, Polished, Bright Annealed, Cold Drawn|
|Packing||Packed in Wooden Boxes, Plastic Bags, Steel Strips Bundled, or as per Customers Requests|
|Specials||Sizes and Specifications other than above can be on request|
|SS 304||1.4301||S30400||SUS 304||304S31||08Х18Н10||Z7CN18‐09||X5CrNi18-10|
|SS 304L||1.4306 / 1.4307||S30403||SUS 304L||3304S11||03Х18Н11||Z3CN18‐10||X2CrNi18-9 / X2CrNi19-11|
|SS 304H||1.4948||S30409||SUS 304H||–||–||–||–|
|SS 304||0.08 max||2 max||0.75 max||0.045 max||0.030 max||18 – 20||–||8 – 11||–|
|SS 304L||0.035 max||2.0 max||1.0 max||0.045 max||0.03 max||18 – 20||–||8 – 13||–|
|SS 304H||0.10 max||2.0 max||0.75 max||0.045 max||0.03 max||18 – 20||–||8 – 10.5||–|
|Density||Melting Point||Tensile Strength||Yield Strength (0.2%Offset)||Elongation|
|8.0 g/cm3||1400 °C (2550 °F)||Psi – 75000 , MPa – 515||Psi – 30000 , MPa – 205||35 %|