Abrasion Resistance Steel 400 Plate is made of quenched and tempered steel. It becomes harder through quenching, tempering, and the addition of carbon and manganese. This process also produces a surface that is impact-resistant, making it suitable for handling abrasive materials like cement, gravel, coal, earth, and more. It excels in situations where there may be sliding or impact abrasion.
What is Abrasion Resistant Steel?
This is wear and tear steel. It has good weldability and formability so it is used in various applications. This steel is flexible in size, and dimensions so customers can form products in any size using this steel. This is making it very useful. Abrasion Resistant 400 offers very powerful chemical and mechanical properties when used in different environmental conditions. This alloy helps the plates to last longer without maintenance problems, so their performance is very significant.
Abrasion Resistant 400 Plates are very good at producing abrasion-resistant properties, which are much more excellent than any other alloy’s abrasion properties. It is basically a wear-and-tear type of steel which makes this alloy the ideal choice for different applications like the petrochemical industry. In addition, it is a very durable product that is highly capable of working for a longer time, even under extreme conditions and, there is no need to invest in maintenance. It is very easy to fabricate, weld, and install in any application.
The features shown by these plates are it constructs very sturdy structures, are very tough product, and possesses higher hardness and strength like mechanical strength, higher yield strength, higher tensile strength, wear resistance, uniform thickness, reliability, etc. These plates show resistance to higher pitting and crevice resistance. It also resists chloride stress cracking corrosion, and resistance to oxidation. The strength and hardness of this plate make it withstand tough environments.
Applications of Abrasion Resistant 400 Plates are
• Construction Machinery
• Fan Industry
• Coal Industry
• Cement Industry
Thickness | 5mm to 150mm |
Width | 1,500mm to 2,500mm |
Length | 6,000mm to 12,000mm |
Heat Treatment | N, Q+T |
Surface Paint | EP, PE, HDP, SMP, PVDF |
Materials | Abrasion Resistant/ Abrex/ rockstar/JFE |
400 BHN Chemical Composition | |||||||||||
Plate | C | Si | Mn | P | S | Cr | Ni | Mo | B | CEV | CET |
3- 6 | 0.15 | 0.70 | 1.60 | 0.025 | 0.01 | 0.50 | 0.25 | 0.25 | 0.004 | 0.41 | 0.28 |
3-(8) | 0.15 | 0.70 | 1.60 | 0.025 | 0.01 | 0.30 | 0.25 | 0.25 | 0.004 | 0.33 | 0.23 |
8 – 20 | 0.15 | 0.70 | 1.60 | 0.025 | 0.01 | 0.50 | 0.25 | 0.25 | 0.004 | 0.37 | 0.27 |
(20)-32 | 0.18 | 0.70 | 1.60 | 0.025 | 0.01 | 1.00 | 0.25 | 0.25 | 0.004 | 0.48 | 0.29 |
(32)-45 | 0.22 | 0.70 | 1.60 | 0.025 | 0.01 | 1.40 | 0.50 | 0.60 | 0.004 | 0.57 | 0.31 |
(45)-51 | 0.22 | 0.70 | 1.60 | 0.025 | 0.01 | 1.40 | 0.50 | 0.60 | 0.004 | 0.57 | 0.38 |
(51)-80 | 0.27 | 0.70 | 1.60 | 0.025 | 0.01 | 1.40 | 1.00 | 0.60 | 0.004 | 0.65 | 0.41 |
(80)-130 | 0.32 | 0.70 | 1.60 | 0.025 | 0.01 | 1.40 | 1.50 | 0.60 | 0.004 | 0.73 | 0.48 |
Mechanical properties of BHN 400 | |||||
Grade | Mechanical Property | Charpy V Impact Test | |||
ABREX 400 | Yield | Tensile | Elongation | Degree | longitudinal |
Min Mpa | Mpa | Min % | -40 | J | |
1000 | 1250 | 10 | 45 |